Chemical composition % of steel C35E (1.1181): EN 10277-5-2008

Cr + Mo + Ni = 0.63

C	Si	Mn	Ni	P	S	Cr	Mo
0.32 - 0.39	max 0.4	0.5 - 0.8	max 0.4	max 0.03	max 0.035	max 0.4	max 0.1

New opportunities for buyers!
Post free buying requirement of steel C35E (1.1181)

Mechanical properties of steel C35E (1.1181)

Nominal thickness (mm):	to 16	16 - 100	100 - 250	250 - 500	500 - 1000

Rm - Tensile strength (MPa) (+N)	550	520	500	480	470

Nominal thickness (mm):	0.3 - 3

Rm - Tensile strength (MPa) (+A)	540

Nominal thickness (mm):	0.3 - 3

Rm - Tensile strength (MPa) (+CR)	930

Nominal thickness (mm):	5 - 10	10 - 16	16 - 40	40 - 63	63 - 100

Rm - Tensile strength (MPa) (+C)	650-1000	600-950	580-880	550-840	520-800

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80

Rm - Tensile strength (MPa) (+QT)	630	600	550	500

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80

ReH - Minimum yield strength (MPa) (+QT)	430	380	320	290

Nominal thickness(mm):	to 16	16 - 100	100 - 250

Re - Upper yield strength or R_p0.2 - 0.2% proof strength (MPa) (+N)	300	270	245

Nominal thickness(mm):	0.3 - 3

R_p0.2 0.2% proof strength (MPa) (+A)	430

Nominal thickness(mm):	to 100	100 - 250	250 - 500	500 - 1000

Re - Upper yield strength (MPa) (+N)	270	245	220	210

Nominal thickness(mm):	5 - 10	10 - 16	16 - 40	40 - 63	63 - 100

R_p0.2 0.2% proof strength (MPa) (+C)	510	420	320	300	270


KV - Impact energy (J) (+QT)	+20° 35


KV - Impact energy (J) (+N)	+20° 27


KV - Impact energy (J) transverse, (+QT)	+20° 22


A - Min. elongation at fracture (%) transverse, (+N)	15

Nominal thickness (mm):	5 - 10	10 - 16	16 - 40	40 - 63	63 - 100

A - Min. elongation at fracture (%) (+C)	6	7	8	9	9

Nominal thickness (mm):	to 8	8 - 20	20 - 50	50 - 80

A - Min. elongation at fracture (%) longitud., (+QT)	17	19	20	20


A - Min. elongation at fracture (%) longitud., (+N)	21


A - Min. elongation at fracture (%) longitud., (+A)	22

Nominal thickness (mm):	to 16	16 - 100	100 - 250

A - Min. elongation Lo = 5,65 √ So (%) (+N)	18	19	19

Brinell hardness (HBW): (+SH)	154 - 207
Brinell hardness (HBW): (+A)	183
Vickers hardness ( HV): (+CR)	275
Vickers hardness ( HV): (+A)	170

Properties of steel C35E (1.1181)

Weldability: It can be welded quite well without any precautions.
Hardenability: Low hardenability; core quenching in water till a diameter of 12-15 mm; as far as bigger diameters are concerned, it hardens only till a certain depth, inversely proportional to diameter, like all nonalloy steels with medium-high carbon content.

Equivalent grades of steel C35E (1.1181)Warning! Only for reference

EU
EN

USA
-

Germany
DIN,WNr

Japan
JIS

France
AFNOR

England
BS

Italy
UNI

Spain
UNE

China
GB

Sweden
SS

Finland
SFS

Russia
GOST

Inter
ISO

C35E

1035

Ck35

S35C

XC38

XC38H1

080M36

CFS6

C35

C35k

F1130

1572

C35

C35E4